性能项目试验条件[状态]测试方法测试数据数据单位基本性能熔体流动速率220℃/10.0kgASTM D-12387.0g/10min物理性能比重ASTM D-7921.07g/cm3模具收缩率Flow,3.20mmASTM D-9550.50-0.70%机械性能拉伸模量ASTM D-6382070MPa拉伸屈服强度ASTM D-63841.4MPa拉伸断裂强度ASTM D-63831.7MPa拉伸屈服伸长率ASTM D-6383.0%拉伸断裂伸长率ASTM D-63824%弯曲模量50.0mm SpanASTM D-7902070MPa弯曲屈服强度50.0mm SpanASTM D-79062.1MPaIZOD缺口冲击强度23℃ASTM D-256288J/m洛氏硬度ASTM D-78595R scale热性能热变形温度0.45MPa，未退火，3.20mmASTM D-64887.8℃热变形温度1.80MPa，未退火，3.20mmASTM D-64878.9℃维卡软化温度ASTM D-152599.4℃CLTEFlow,-40TO40℃ASTM E-8318.6cm/cm/℃CLTETransverse,-40TO40℃ASTM E-8319.2cm/cm/℃